[pt] CONTRIBUIÇÃO NA AVALIAÇÃO DA VIDA ÚTIL DE EIXO VIRABREQUIM SOB FADIGA MULTIAXIAL

[en] CONTRIBUTION IN THE USEFUL LIFE EVALUATION OF CRANKSHAFT UNDER MULTIAXIAL FATIGUE

[pt] ROBERTA AMORIM DE MAGALHAES MONTEIRO GONCALVES

[pt] USINA TERMOELETRICA

[pt] EIXOS VIRABREQUINS

[pt] FADIGA DE ALTO CICLO

[pt] CARREGAMENTOS EM FASE E FORA DE FASE

[pt] ACO ESTRUTURAL

[en] THERMOELECTRIC PLANT

[en] CRANKSHAFTS

[en] HIGH CYCLE FATIGUE

[en] IN-PHASE AND OUT-OF-PHASE LOADS

[en] STRUCTURAL STEEL

[pt] As previsões de falhas por fadiga tornam-se críticas sob condições multiaxiais de carregamento, uma vez que a complexidade do estado de tensões requer uma análise com base em modelos mais avançados do que aqueles adotados para carregamentos uniaxiais. Neste contexto, alguns critérios foram desenvolvidos para tentar prever a falha de componentes submetidos a carregamentos cíclicos multiaxiais. Um exemplo de componente mecânico sujeito a fadiga multiaxial quando em serviço são os eixos virabrequim de unidades geradoras de plantas termoelétricas. Usualmente projetados segundo o critério de Findley, falhas recentes de eixos virabrequim ocorridas no parque termoelétrico nacional, tem provocado o questionamento da eficiência de tal critério. Desta forma, o presente estudo teve como objetivo analisar a aplicabilidade de seis modelos (Papadopoulos, Findley, Matake, McDiarmid, Carpinteri e Spagnoli e Liu e Mahadevan) de fadiga multiaxial de alto ciclo, baseados no plano crítico, para prever a falha de eixos virabrequim de unidades geradoras. Para aplicação dos modelos, adotaram-se diferentes parâmetros de carregamento (tensão média e defasagem de aplicação das tensões normais e cisalhantes) e propriedades de material (resistência à fadiga), partindo de valores encontrados na literatura. Observou-se uma divergência entre os resultados de cada modelo estudado, sendo uns mais conservadores do que os outros, em função do carregamento e propriedades do material. Entretanto, o modelo de Papadopoulos, com base na facilidade de aplicação e sensibilidade de previsão da falha, mostrou-se mais adequado.

[en] The fatigue failure prediction becomes critical under multiaxial loading conditions, since the complexity of the stress state requires analysis based on models more advanced than those adopted for uniaxial loads. In this context, some criteria were developed in an attempt to predict the failure of components subjected to multiaxial cyclic loads. An example of mechanical component subject to multiaxial fatigue is the crankshaft of thermoelectric plants. It is usually projected according to the Findley criterion. However, recent failures of crankshafts occurring in the national thermoelectric park, put on doubt the efficiency of such criterion. In this way, the present study aimed to analyze the applicability of six models (Papadopoulos, Findley, Matake, McDiarmid, Carpinteri e Spagnoli and Liu e Mahadevan) of high cycle multiaxial fatigue, based on the critical plane, to predict failure on crankshaft of generating units. For the models application, different loading parameters (medium stress and out-of-phase stresses) and material properties (fatigue limit) were adopted, starting from values found in the literature. A divergence between the results of each model was observed, some of them were more conservative than the others, depending on the loading and material s properties. However, the Papadopoulos model, based on easy application and failure prediction sensitivity, proved to be more suitable than the others.

MARCOS VENICIUS SOARES PEREIRA

FATHI AREF IBRAHIM DARWISH

MARCOS VENICIUS SOARES PEREIRA

ARNALDO FREITAS CAMARÃO

GILVANIA TERTO ALVES

RICARDO PONDE WEBER

2019-01-30

2017-09-19

[pt] TEXTO

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

PORTUGUÊS

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=36348@1

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=36348@2

https://doi.org/10.17771/PUCRio.acad.36348