Título: | EVALUATION OF THE RESISTANCE TO SULPHIDE STRESS CORROSION CRACKING AND HYDROGEN EMBRITTLEMENT OF API 5L -X80 GIRTH WELDS | |||||||
Autor: |
ADRIANA FORERO BALLESTEROS |
|||||||
Colaborador(es): |
IVANI DE SOUZA BOTT - Orientador JOSE ANTONIO DA CUNHA PONCIANO GOMES - Coorientador |
|||||||
Catalogação: | 17/JAN/2018 | Língua(s): | PORTUGUESE - BRAZIL |
|||||
Tipo: | TEXT | Subtipo: | THESIS | |||||
Notas: |
[pt] Todos os dados constantes dos documentos são de inteira responsabilidade de seus autores. Os dados utilizados nas descrições dos documentos estão em conformidade com os sistemas da administração da PUC-Rio. [en] All data contained in the documents are the sole responsibility of the authors. The data used in the descriptions of the documents are in conformity with the systems of the administration of PUC-Rio. |
|||||||
Referência(s): |
[pt] https://www.maxwell.vrac.puc-rio.br/projetosEspeciais/ETDs/consultas/conteudo.php?strSecao=resultado&nrSeq=32706&idi=1 [en] https://www.maxwell.vrac.puc-rio.br/projetosEspeciais/ETDs/consultas/conteudo.php?strSecao=resultado&nrSeq=32706&idi=2 |
|||||||
DOI: | https://doi.org/10.17771/PUCRio.acad.32706 | |||||||
Resumo: | ||||||||
The susceptibility of pipeline steels to stress corrosion cracking (SCC) depends on a series of factors ranging from the manufacture of the steel, the pipe fabrication, the assembly of the pipeline and the type of substances to be transported. Additionally, the welding procedures adopted during the production
of the tubes and for construction of the pipelines (field welding), can modify the properties of the base metal in the heat affected zone (HAZ), potentially rendering this region susceptible to sulphide stress corrosion cracking and hydrogen embrittlement.This study evaluates the resistance of girth welds in API 5LX80 pipes to hydrogen embrittlement and also to stress corrosion cracking in the presence of sulphides. The evaluation was performed according to NACE TM0177/96, Method A, applying the criterion of fracture/no fracture, and slow strain rate tensile tests (SSRT) were undertaken using a sodium thiosulphate
solution according to the ASTM G29 standard. According to the requirements of the NACE TM0177/96 test, the base metal was considered approved. The weld metal exhibited susceptibility to SCC in the presence of sulphides, failling in a period of less than 720h. The susceptibility of the welded joint to SCC in the presence of sulphides was confirmed by the results obtained with SSRT tensile tests, where a significant decrease in the ultimate tensile strength, elongation and time to fracture were observed. The mechanism of fracture for the tests was predominantly transgranular.
|
||||||||