[pt] METAIS DE SOLDA LIGADOS AO NI COM ADIÇÕES DE CU E MO PARA SOLDAGEM SUBAQUÁTICA MOLHADA

[en] NI ALLOYED WELD METALS WITH ADDITIONS OF CU AND MO FOR UNDERWATER WET WELDING

[pt] ANA PAULA BECK LEAO

[pt] ELETRODOS

[pt] CARACTERIZACAO MICROESTRUTURAL

[pt] SOLDAGEM

[en] ELETRODE

[en] MICROSTRUCTURAL CHARACTERIZATION

[en] WELDING

[pt] Este trabalho foi desenvolvido com o objetivo de melhorar as propriedades mecânicas dos metais de solda produzidos por eletrodos oxidantes com níquel, juntamente com adições de cobre e de molibdênio, através do refino de grão ou do endurecimento por solução sólida. Os eletrodos oxidantes se caracterizam por apresentar menores teores de hidrogênio difusível quando comparado aos eletrodos rutílicos. Entretanto o metal de solda depositado com este tipo de eletrodo possui propriedades mecânicas inferiores aos eletrodos rutílicos, já que elementos de liga importantes, como Mn e Si, são perdidos por oxidação. Com a intenção de contornar esta situação procurou-se adicionar elementos de liga que não sejam significantemente afetados pelo caráter oxidante do revestimento, como Cu ou Mo. Foram preparados dois corpos de prova para soldagem, nos quais foram usinados furos espaçados e um rasgo para adição de ambos elementos, Cu e Mo. As diferentes porcentagens destes elementos foram medidas através da microanálise por Espectroscopia de Energia Dispersiva. A partir desses resultados foi realizada análise microestrutural utilizando a Microscopia Ótica, medidas do tamanho de grão, além do ensaio de microdureza para avaliar a influência de cada elemento no metal de solda. Os resultados mostraram que o molibdênio teve uma forte influência na microdureza do metal de solda quando comparado ao cobre. Em relação ao tamanho de grão, eles apresentaram influências opostas, a adição de maiores teores Mo acarretou uma diminuição do tamanho de grão e a com a adição do Cu ocorreu um pequeno aumento do grão até tornar-se constante.

[en] This work was carried out to improve the mechanical properties of weld metals deposited by nickel oxidizing electrodes, together with additions of copper and molybdenum, through the grain refinement or by solid solution hardening. The oxidizing electrodes are characterized by the lower levels of diffusible hydrogen and, hence, by the lesser possibility of cold crack formation when compared to rutile electrodes. However, the weld metal deposited with this type of electrode shows mechanical properties below that obtained by rutile electrodes, as long as important alloy elements, such as Mn and Si, are lost by oxidation. In order to avoid this situation and obtain weld metals with better mechanical properties it was added alloy elements that are not significantly affected by the oxidant character of the coating, such as Cu and Mo. Two test specimens were prepared for welding, where spaced holes and a notch were machined in each one for the addition of both elements, Cu and Mo. Different percentages of these elements were measured by Energy Dispersive Spectroscopy microanalysis. From these results it was performed microstructural analysis using optical microscopy, grain size measurements and microhardness tests to evaluate the influence of each element in the weld metal and compare them to each other. The results showed that molybdenum has a stronger influence on the microhardness of the weld metal than copper. Regarding the grain size it was noted an opposite influence of the elements, where the addition of Mo caused a decrease of the grain size and the addition of Cu caused a slightly increase, until the grain size becomes constant.

IVANI DE SOUZA BOTT

VALTER ROCHA DOS SANTOS

IVANI DE SOUZA BOTT

VALTER ROCHA DOS SANTOS

ALEXANDRE MEIRELLES POPE

EZEQUIEL CAIRES PEREIRA PESSOA

GIOVANI DALPIAZ

2010-03-04

2009-09-04

[pt] TEXTO

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

PORTUGUÊS

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=15335@1

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=15335@2

https://doi.org/10.17771/PUCRio.acad.15335