[pt] EFEITO DA TEMPERATURA DE AUSTENITIZAÇÃO NO PROCESSO DE TÊMPERA E PARTIÇÃO

[en] EFFECT OF THE AUSTENITIZATION TEMPERATURE ON THE QUENCHING AND PARTITIONING PROCESS

[pt] DANIEL MASSARI DE SOUZA COELHO

[pt] TRATAMENTOS TERMICOS

[pt] TRANSFORMACAO DE FASE

[pt] AUSTENITA RETIDA

[pt] PARTICAO DE CARBONO

[pt] ACO

[en] HEAT TREATMENTS

[en] PHASE TRANSFORMATION

[en] RETAINED AUSTENITE

[en] CARBON PARTITIONING

[en] STEEL

[pt] O processo de Têmpera e Partição (T&P) possibilita a produção de aços com frações controladas de austenita retida, a partir do enriquecimento da austenita pela partição de carbono da martensita sem a precipitação de carbonetos. A austenita retida proporciona o efeito TRIP (plasticidade induzida por transformação), que confere ao material uma deformação uniforme e uma melhor absorção de energia durante o impacto. Os aços produzidos por este processo atendem principalmente às necessidades da indústria automobilística, que busca aços com melhores propriedades para a diminuição de peso e aumento da segurança dos automóveis. Nesta dissertação, ligas de aço com diferentes composições e tamanhos de grão foram produzidos pelo processo de Têmpera e Partição e a fração de austenita retida foi medida por difração de raios-X. As ligas também foram caracterizadas por nanoindentação, microscopia ótica e microscopia eletrônica de varredura. As amostras estudadas foram produzidas com uma austenitização completa a 930°C, realizada para promover um aumento no tamanho de grão, e os resultados foram comparados com amostras estudadas anteriormente com temperatura de austenitização de 890°C. Os resultados obtidos indicaram um aumento da fração de austenita retida com o aumento do grão austenítico original. Estes resultados foram interpretados com base no modelo teórico desenvolvido para o processo T&P.

[en] The Quenching and Partitioning (Q&P) process allows the production of steels with controlled fractions of retained austenite from the enrichment of the austenite by carbon partitioning from the martensite without carbide precipitation. The retained austenite is responsible for the TRIP effect (transformation induced plasticity), which enhances the material behavior providing a uniform strain and a better energy absorption during impact. Steels produced by this process match the requirements of the automotive industry, which looks for weight reduction and safety improvements in cars. In the present dissertation, steels with different compositions and grain sizes were produced by the Quenching and Partition process and their retained austenite fraction was measured by x-ray diffraction. The steels were also characterized by nanoindentation, optical microscopy and scanning electron microscopy. The specimens studied were produced by a complete austenitization at 930°C, to promote an increase in the austenitic grain size, and the results were compared with previously studied specimens produced by a complete austenitization at 890°C. The experimental results indicate an increase of austenite fraction with an increase in grain size of the original austenite. These results were analyzed based on the theoretical model develop for the Q&P process.

FERNANDO COSME RIZZO ASSUNCAO

ROBERTO RIBEIRO DE AVILLEZ

FERNANDO COSME RIZZO ASSUNCAO

ANA ROSA FONSECA DE AGUIAR MARTINS

ANDRE LUIZ VASCONCELLOS DA COSTA E SILVA

2008-09-11

2008-04-17

[pt] TEXTO

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

application/pdf

PORTUGUÊS

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=12177@1

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=12177@2

https://doi.org/10.17771/PUCRio.acad.12177