Título: | INDUCTION HOT BENDING OF STEEL PIPE API 5L X80 | ||||||||||||||||||||||||||||||||||||
Autor: |
GILMAR ZACCA BATISTA |
||||||||||||||||||||||||||||||||||||
Colaborador(es): |
IVANI DE SOUZA BOTT - Orientador |
||||||||||||||||||||||||||||||||||||
Catalogação: | 12/JUL/2006 | Língua(s): | PORTUGUESE - BRAZIL |
||||||||||||||||||||||||||||||||||
Tipo: | TEXT | Subtipo: | THESIS | ||||||||||||||||||||||||||||||||||
Notas: |
[pt] Todos os dados constantes dos documentos são de inteira responsabilidade de seus autores. Os dados utilizados nas descrições dos documentos estão em conformidade com os sistemas da administração da PUC-Rio. [en] All data contained in the documents are the sole responsibility of the authors. The data used in the descriptions of the documents are in conformity with the systems of the administration of PUC-Rio. |
||||||||||||||||||||||||||||||||||||
Referência(s): |
[pt] https://www.maxwell.vrac.puc-rio.br/projetosEspeciais/ETDs/consultas/conteudo.php?strSecao=resultado&nrSeq=8660&idi=1 [en] https://www.maxwell.vrac.puc-rio.br/projetosEspeciais/ETDs/consultas/conteudo.php?strSecao=resultado&nrSeq=8660&idi=2 |
||||||||||||||||||||||||||||||||||||
DOI: | https://doi.org/10.17771/PUCRio.acad.8660 | ||||||||||||||||||||||||||||||||||||
Resumo: | |||||||||||||||||||||||||||||||||||||
The present work discusses the effect of the induction
bending process on
the microstructure and the mechanical properties of an API
5L X80, 20 pipe
produced by the UOE process. The key characteristic of the
pipe was the
manufacturing process of the steel plate, involving
thermomechanical controlled
rolling without accelerated cooling. The pipe bending was
carried out applying
local induction heating followed by water quenching and a
further temper heat
treatment was applied to the curved section. The
methodology of analysis
compared the curved section with the original body pipe,
taking into account
dimensional analysis, microstructural evaluation and
mechanical tests which
included Charpy-V impact, tensile and microhardness. A
significant
microstructural change and decrease, not only in the
transition temperature, but
also in the yield strength ocurred after induction
bending, this reduction was
below the standard requirements. The subsequent tempering
heat treatment
applied to the curved section produced an increase in the
yield strength to achieve
the API 5L requirements for this class of steel.
|
|||||||||||||||||||||||||||||||||||||
|