Zirconia-based materials present excellent mechanical properties, tenacity, chemical, and dimensional stability as well as their Young modulus is similar to stainless steel alloys. Due to these characteristics, zirconia has been largely applied in the fabrication of dental prostheses. Modifications in the zirconia composition and the development of CAD-CAM systems has allowed zirconia-based restorations to become a common clinical procedure in current dentistry. Fully sintered and homogeneous blocks from industry are machined at controlled environments seeking to obtain the desired geometry of the restorations. After the machining process, the restorations are sintered to improve their density. This process reduces the failures caused by manual and laboratorial manipulations during fabrication procedure. The aim of this study is to evaluate the effect of hydrothermal aging and sandblasting with aluminum oxide on the mechanical properties of three Yttria-containing tetragonal zirconia polycrystalline (Y-TZP). Three types of Y-TZP, containing different yttria dioxide, were used in the study: Y-TZP with 5,2 per cent mol Y2O3 (Prettau Anterior Super-Translúcida da Zirkonzahn), Y-TZP with 3 per cent mol de Y2O3 (VIPI Block Zirconn) and Y-TZP with 3 per cent mol Y2O3 and optimized translucency (VIPI Block Zirconn Translucent). All the zirconias are indicated for being used as monolithic restorations. 15 specimens from each zirconia tested were sintered and distributed to three groups according to the surface treatment and the aging process. In the group I, the specimens were sandblasted with aluminum oxide particles. For the group II, the zirconia specimens were abraded and polished. In the group III, the specimens were abraded, polished, recovered and aged in a reactor controller for 5 hours at 134 degrees Celsius and 2 bar. The characterization of the zirconia microstructure has been carried out by means of: X-ray diffraction, relative density, Raman spectroscopy, Vickers microhardness, superficial roughness. In addition, the average grain size analysis by scanning electron microscopy were made. The results show that the relative density values were above 99 per cent, and that the hydrothermal aging causes monoclinic phase transformation and affects flexural strength values. However, the clinical indications of materials did not change. The average grain size was between 0.367 and 0.621. The microhardness and tenacity values of materials did not change by yttria concentration or crystallographic phases. The roughness values were not significantly affected by the hydrothermal aging. On the other hand, the flexural strength values were affected by sandblasting process and clinical indication of ceramics tested was changed.