[pt] PROCESSOS DE PRECIPITAÇÃO INTERGRANULAR E VOLUMÉTRICA NA LIGA 33 (FE-NI-CR-MO-N)
Título
[en] RECIPITATION PROCESSES CONTROLLED BY LATTICE AND GRAIN BOUNDARY DIFFUSION IN ALLOY 33 (FE-NI-CR-MO-N)
Autor
[pt] VIVIANE DELVAUX CARNEIRO
Vocabulário
[pt] PRECIPITACAO DESCONTINUA
Vocabulário
[pt] PARTICAO DE SOLUTOS
Vocabulário
[pt] REACOES CONCOMITANTES
Vocabulário
[en] DISCONTINUOUS PRECIPITATION
Vocabulário
[en] SOLUTE PARTITIONING
Vocabulário
[en] SIMULTANEOUS REACTIONS
Resumo
[pt] Este trabalho é uma investigação da microestrutura e
cinética dos fenômenos de precipitação que ocorrem na Liga
33 (Fe-Ni-Cr-Mo-Cu-N), sistema metálico desenvolvido pela
Krupp VDM com o intuito de suportar altas temperaturas e
ambiente corrosivo. A Liga 33 incorre precipitação
contínua e descontínua simultaneamente, como resultado do
tratamento de envelhecimento realizado numa faixa de
temperatura correspondente àquela que o material atinge
quando submetido a um processo de soldagem. A
caracterização microestrutural foi realizada por
microscopia ótica, microscopia eletrônica de varredura, e
microscopia eletrônica de transmissão, incluindo
microanálise, devido à ordem de grandeza nanométrica das
fases precipitadas. A precipitação descontínua ocasiona
uma estrutura lamelar no contorno dos grãos, resultado do
crescimento cooperativo entre as lamelas, envolvendo
átomos substitucionais (Cr, por exemplo) e intersticiais
(N). A precipitação contínua ocorre no interior dos grãos
gerando precipitados com diferentes morfologias. A
microanálise revela que os produtos gerados em ambas as
reações crescem competindo pelo Cr. Uma análise cinética-
morfológica aponta para a natureza não estacionária da
reação descontínua, que sofre gradativa diminuição de sua
taxa de transformação, até ser totalmente paralisada.
Resumo
[en] This work is an investigation of the microstructure and
kinetics of the phenomena occurring inside Alloy 33 (Fe-Ni-
Cr-Mo-Cu-N), a metallic system developed by Krupp VDM to
endure high temperatures and corrosive environment. Alloy
33 incurs continuous and discontinuous precipitation
simultaneously, as a result of the aging treatment induced
in a temperature range correspondent to the one of a
welding process in the referred material. The
microstructural characterization was performed by optical
microscopy, scanning electron microscopy and transmission
electron microscopy, including microanalysis, due to the
nanometric nature of the precipitated phases.
Discontinuous precipitation produces a lamellar structure
along grain boundaries as a result of a cooperative growth
between the lamellae, involving substitucional and
interstitial atoms, Cr and N respectively. Continuous
precipitation occurs inside grains, generating
precipitates with different morphologies. Microanalysis
reveals that products of both precipitation reactions grow
competing for Cr. A kinetic-morphological analysis points
to the non-stationary characteristic of the discontinuous
precipitation, where the transformation rate diminishes
until it stops completely, as aging occurs.
Orientador(es)
IVAN GUILLERMO SOLORZANO NARANJO
Banca
SIDNEI PACIORNIK
Banca
IVAN GUILLERMO SOLORZANO NARANJO
Banca
ANGELO FERNANDO PADILHA
Catalogação
2005-02-10
Apresentação
2004-07-29
Tipo
[pt] TEXTO
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Idioma(s)
PORTUGUÊS
Referência [pt]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=5927@1
Referência [en]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=5927@2
Referência DOI
https://doi.org/10.17771/PUCRio.acad.5927
Arquivos do conteúdo
CAPA, AGRADECIMENTOS, RESUMO, ABSTRACT, SUMÁRIO E LISTAS PDF CAPÍTULO 1 PDF CAPÍTULO 2 PDF CAPÍTULO 3 PDF CAPÍTULO 4 PDF CAPÍTULO 5 PDF CAPÍTULO 6 PDF REFERÊNCIAS BIBLIOGRÁFICAS PDF