[en] PREDICTION OF TOLERANCE TO SHORT CRACKS DEPARTING FROM NOTCHED SPECIMENS

[pt] PREVISÃO DA TOLERÂNCIA ÀS TRINCAS CURTAS QUE NASCEM DE ENTALHES

[pt] GABRIELA CRISTINA PAIVA MARTINS

[pt] FADIGA

[pt] MODELAGEM DAS TRINCAS CURTAS

[pt] TAMANHO CARACTERISTICO DE TRINCA CURTA

[pt] VIDA A FADIGA

[pt] LIMIAR DE PROPAGACAO

[pt] TRINCA CURTA

[en] FATIGUE

[en] SHORT CRACK MODELING

[en] FATIGUE SHORT CRACK THRESHOLD

[en] FATIGUE LIFE

[en] GROWTH THRESHOLD

[en] SHORT CRACK

[pt] Para garantir que um componente estrutural resistirá ao longo de sua campanha operacional às trincas que podem não ter sido detectadas durante a última inspeção, é preciso estudar a tolerância aos defeitos nos componentes estruturais. As trincas longas podem ser modeladas por conceitos tradicionais da Mecânica da Fratura, mas as trincas curtas, em especial aquelas que partem de entalhes, não podem. O comportamento destas trincas curtas é modelado a partir do conceito do seu tamanho característico a0, proposto por El Haddad, Topper e Smith, que concilia o limite de iniciação de uma trinca por fadiga com o limiar de propagação das trincas longas. Para obtenção deste parâmetro, o limite de fadiga SL da liga de Al 6351-T6 é estimado por termografia e verificado extrapolando sua curva eN medida por procedimentos normalizados para uma vida útil muito longa. O limiar de propagação das trincas longas DeltaKth é medido através de ensaios padronizados. Por último, tamanhos de trincas em corpos de prova de geometrias diferentes são previstos por aproximações analíticas a partir dos campos de tensões à frente dos entalhes Sigma y(x)/Sigma n por Inglis e Creager e Paris.

[en] To guarantee the structural integrity of a component during its operational life, it is necessary to study the tolerances to defects. Long cracks may be modeled by traditional concepts of Fracture Mechanics, but short cracks, especially those that start from notches, cannot. The behavior of these short cracks is modeled on the concept of characteristic size a0, presented by El Haddad, Topper and Smith, which reconciles the initiation limit of a fatigue crack with the propagation threshold of the long crack. To obtain this parameter, the fatigue limit SL is estimated by thermography, and thereafter, the result of the Al 6351-T6 alloy, presented in this work, is verified by extrapolating its eN curve measured by standard procedures for a very long service life. The propagation threshold of long cracks Kth is measured by the standard test. Finally, crack sizes in specimens for different geometries are predicted by analytical approximations from the stress fields ahead of the notches by Inglis and Creager and Paris.

JAIME TUPIASSU PINHO DE CASTRO

JAIME TUPIASSU PINHO DE CASTRO

MARCO ANTONIO MEGGIOLARO

ANTONIO CARLOS DE OLIVEIRA MIRANDA

2020-11-05

2019-09-26

[pt] TEXTO

application/pdf

PORTUGUÊS

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=50215@1

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=50215@2

https://doi.org/10.17771/PUCRio.acad.50215