Título: | STUDY OF THE INFLUENCE OF MICROSTRUCTURAL DEFECTS ON THE FATIGUE THRESHOLD OF STRUCTURAL STEELS | ||||||||||||
Autor: |
LETICIA BUENO NOGUEIRA |
||||||||||||
Colaborador(es): |
MARCOS VENICIUS SOARES PEREIRA - Orientador |
||||||||||||
Catalogação: | 17/MAI/2021 | Língua(s): | PORTUGUESE - BRAZIL |
||||||||||
Tipo: | TEXT | Subtipo: | THESIS | ||||||||||
Notas: |
[pt] Todos os dados constantes dos documentos são de inteira responsabilidade de seus autores. Os dados utilizados nas descrições dos documentos estão em conformidade com os sistemas da administração da PUC-Rio. [en] All data contained in the documents are the sole responsibility of the authors. The data used in the descriptions of the documents are in conformity with the systems of the administration of PUC-Rio. |
||||||||||||
Referência(s): |
[pt] https://www.maxwell.vrac.puc-rio.br/projetosEspeciais/ETDs/consultas/conteudo.php?strSecao=resultado&nrSeq=52736&idi=1 [en] https://www.maxwell.vrac.puc-rio.br/projetosEspeciais/ETDs/consultas/conteudo.php?strSecao=resultado&nrSeq=52736&idi=2 |
||||||||||||
DOI: | https://doi.org/10.17771/PUCRio.acad.52736 | ||||||||||||
Resumo: | |||||||||||||
The determination of the fatigue crack propagation threshold offers a range
of materials utilization in engineering, in application to projects that are tolerant to
damage. [delta]Kth is a tool that allows the establishment of a loading criterion under
which the cracks will not grow significantly during the service operations of the
component. For its determination to be widely applied, it was necessary to establish
and study the factors that could influence it positively or negatively. Among them,
the microstructure was of great importance because it had to be controlled from the
material manufacturing to the placing putting into service of a finished component.
The aim of the component and the stresses to which it is subjected when in service
determine the material selection. Thus, basic characteristics and minimum
requirements were listed which have attend the safety and has reduced cost-benefit
ratio. Materials (SAE 4340 and SAE 4140) were selected whose chemical
composition and mechanical properties that were similar to DIN 42CrMo4 so that
they could serve as an alternative in the use of crankshafts to propose a solution in
the practical problem which they were breaking well below the limit fatigue life
that they proposed. The results obtained were satisfactory because in the fracture
toughness tests of one of the chosen materials (SAE 4140) [delta]Kth of 12.48 MPa[square root]m
was obtained and in the reference material, [delta]Kth(average) of 6.1 MPa[square root]m. The
observation of the microstructure of the reference material may indicate, with
restrictions, as a corroboration of the result presented in the [delta]Kth, because
occurrences of dispersed inclusions in the steel matrix.
|
|||||||||||||
|