[pt] ESTUDO DA FORMAÇÃO DE INCRUSTAÇÕES INORGÂNICAS EM MEMBRANAS DE NANOFILTRAÇÃO UTILIZADAS EM PROCESSOS DE DESSULFATAÇÃO
Título
[en] INORGANIC FOULING IN NANOFILTRATION MEMBRANES DURING DESULPHATATION PROCESS
Autor
[pt] THAIS DE LIMA ALVES
Vocabulário
[pt] MEMBRANAS
Vocabulário
[pt] INCRUSTACAO INORGANICA
Vocabulário
[pt] DESSULFATACAO
Vocabulário
[pt] NANOFILTRACAO
Vocabulário
[en] MEMBRANE
Vocabulário
[en] INORGANIC FOULING
Vocabulário
[en] FOULING
Vocabulário
[en] NANOFILTRATION
Resumo
[pt] Um problema inerente ao processo de separação por
membranas, mais
especificamente a nanofiltração( NF) é a perda de
eficiência das membranas com
o tempo de operação do sistema, que se deve, em grande
parte, ao depósito ou
adsorção de material na superfície e/ou poros das
membranas. O desenvolvimento
de incrustações faz com que o fluxo permeado diminua muito
e torna necessário
regimes freqüentes de limpeza que ocasionam uma acentuada
diminuição na vida
útil da membrana. Este estudo enfoca o comportamento de
soluções salinas
simples, binárias e multicomponentes submetidas a processo
de nanofiltração com
membrana comercial utilizada em processos de dessulfatação
(NF-90-400- Dow)
em módulo de placa e quadros com alimentação em fluxo
cruzado, condições de
pressão elevada e baixa vazão escolhidas de modo a
favorecer a formação dos
depósitos. A membrana selecionada para o estudo mostrou
grande eficiência na
eliminação de sulfato tanto para soluções simples como
para soluções binárias, foi
observado que variação na força iônica afeta a eficiência
de remoção de sulfatos
das correntes de alimentação e ainda que variações na
diferença de pressão
aplicada no processo utilizando água do mar sintética como
solução de operação
afetam de forma significativa as características de
incrustação.
Resumo
[en] Fouling is a problem without a satisfactory solution in
nanofiltration process.
The fouling development causes low performance and
reduction of the membrane
time life. The aim of this work was to evaluate the
behavior of salts significantly
present in the sea water in fouling formation on the
membrane surface. A
commercial nanofiltration membrane (NF-90-400), which was
developed for
sulphates removal process, was particularly investigated.
The permeation
experiments with sulphates solution were carried out
during seven days; permeate
flux and effluent conductivities were monitored.
Temperature, transmembrane
pressure, concentration, and flow velocity of the feeding
solution were kept in
25ºC, 30 bar, 4.000 mg/L, and 0,030 m/s, respectively. The
selected membrane
showed great efficiency in the sulphate elimination for
simple solutions and for
binary solutions, it was observed that variation in the
ionic force affects the
efficiency of sulphates removal. Variations in DP when the
solution of work was
synthetic sea water affects in a significant way the
incrustation characteristics.
Orientador(es)
OLAVO BARBOSA FILHO
Banca
MARCOS HENRIQUE DE PINHO MAURICIO
Banca
FRANCISCO JOSE MOURA
Banca
LIDIA YOKOYAMA
Banca
OLAVO BARBOSA FILHO
Banca
GANDHI GIORDANO
Catalogação
2006-10-27
Apresentação
2006-04-10
Tipo
[pt] TEXTO
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Idioma(s)
PORTUGUÊS
Referência [pt]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=9206@1
Referência [en]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=9206@2
Referência DOI
https://doi.org/10.17771/PUCRio.acad.9206
Arquivos do conteúdo
CAPA, AGRADECIMENTOS, RESUMO, ABSTRACT, SUMÁRIO E LISTAS PDF CAPÍTULO 1 PDF CAPÍTULO 2 PDF CAPÍTULO 3 PDF CAPÍTULO 4 PDF CAPÍTULO 5 PDF CAPÍTULO 6 PDF CAPÍTULO 7 PDF CAPÍTULO 8 PDF CAPÍTUTO 9 PDF CAPÍTULO 10 PDF REFERÊNCIAS BIBLIOGRÁFICAS E ANEXOS PDF