[pt] ANÁLISE DE FILMES POLIMÉRICOS DENSOS DE ACC/PHAMCL POR TÉCNICAS DE DSC, DMA, XPS, ÂNGULO DE CONTATO E AFM
Título
[en] DSC, DMA, XPS, CONTACT ANGLE E AFM ANALYSIS OF DE ACC/PHAMCL THICK FILMS SURFACES
Autor
[pt] SAMANTHA FONSECA DOS SANTOS
Vocabulário
[pt] FISICA
Vocabulário
[pt] CALORIMETRIA DIFERENCIAL EXPLORATORIA
Vocabulário
[pt] ANGULO DE CONTATO
Vocabulário
[pt] MICROSCOPIA DE FORCA ATOMICA
Vocabulário
[pt] ANALISE DINAMICA
Vocabulário
[en] PHYSICS
Vocabulário
[en] DIFFERENTIAL SCANNING CALORIMETRY
Vocabulário
[en] CONTACT ANGLE
Vocabulário
[en] ATOMIC FORCE MICROSCOPY
Vocabulário
[en] DYNAMIC ANALYSIS
Resumo
[pt] Neste trabalho, foram estudadas filmes poliméricos densos
formadas por acetato de celulose (AcC) e
polihidroxialkanoato de cadeia
média PHAmcl, com diferentes concentrações relativas de
cada polímero.
Os filmes de PHAmcl/DAC foram preparadas a partir de
soluções
poliméricas, diluídas em dimetil cetona, na qual se
realiza uma mistura
com agitação contínua. Foram preparadas as amostras: AcC
puro,
PHAmcl puro e seis misturas com concentrações variando
de
2 porcento a 12 porcento
(m/v) de PHAmcl em AcC. Medidas de calorimetria
diferencial exploratória
e análise dinâmica mecânica foram realizadas a fim de se
conhecer a
miscibilidade das blendas formadas A composição química
das
superfícies desses filmes foi caracterizada utilizando a
técnica de
espectroscopia de fotoelétrons induzida por raios-X
(XPS).
A morfologia e
as propriedades mecânicas das amostras foram estudadas
com
o auxílio
da microscopia de força atômica (AFM). Observou-se nas
misturas um
enriquecimento na superfície de PHAmcl e uma alteração
da
morfologia
para toda a superfície com a incorporação de PHAmcl. Foi
observada
uma diminuição na dureza com o aumento a concentração de
PHAmcl no
filmes. Os filmes apresentaram miscibilidade até 10
porcento
PHAmcl/90porcentoAcC
em volume.
Resumo
[en] In this work, the study of thick films formed by cellulose
acetate and
medium chain length polyhydroxyalkanotes with different
molar
concentration of PHB is presented. The films were prepared
by polymeric
solutions diluted in dimethil ketone with continued
agitation. The solvent
evaporation occurs on a glass plate in controlled
atmosphere of 300 C.
Eight samples were prepared: pure AcC and PHAmcl and
mixtures with
PHAmcl bulk concentrations in the range of 2 to 12 percent
(w/v).
Differential
scanning calorimetry and dynamic mechanical analysis
measurements
were performed in order to know the samples miscibility.
The surface
chemical composition of the samples was characterized by X-
ray
photoelectron spectroscopy (XPS). The morphology and
mechanical
properties were studied by atomic force microscopy (AFM).
PHAmcl
surface enrichment and morphology modification of the
films were
observed on the whole surface with the increasing of
PHAmcl. A decrease
in the films hardness was observed for increasing PHAmcl
bulk
concentration. The films were found to be miscible until
10percentPHAmcl/90percentAcC bulk concentration.
Orientador(es)
RODRIGO PRIOLI MENEZES
Coorientador(es)
RUBEN JESUS SANCHEZ RODRIGUEZ
Banca
GILSON BRAND BAPTISTA
Banca
RODRIGO PRIOLI MENEZES
Banca
VALERIA BATISTA NUNES
Banca
RUBEN JESUS SANCHEZ RODRIGUEZ
Catalogação
2006-03-10
Apresentação
2005-08-19
Tipo
[pt] TEXTO
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Idioma(s)
PORTUGUÊS
Referência [pt]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=7887@1
Referência [en]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=7887@2
Referência DOI
https://doi.org/10.17771/PUCRio.acad.7887
Arquivos do conteúdo
CAPA, AGRADECIMENTOS, RESUMO, ABSTRACT, SUMÁRIO E LISTAS PDF CAPÍTULO 1 PDF CAPÍTULO 2 PDF CAPÍTULO 3 PDF CAPÍTULO 4 PDF CAPÍTULO 5 PDF REFERÊNCIAS BIBLIOGRÁFICAS PDF