[pt] ANÁLISE EXPERIMENTAL DA ADERÊNCIA ENTRE O CONCRETO E COMPÓSITOS COM TECIDO DE FIBRAS DE CARBONO
Título
[en] EXPERIMENTAL ANALISYS ON BOND BETWEEN CONCRETE AND CARBON FIBER COMPOSITES FABRIC
Autor
[pt] JULIANA MARTINELLI MENEGHEL
Vocabulário
[pt] REFORCO ESTRUTURAL
Vocabulário
[pt] ADERENCIA
Vocabulário
[pt] COMPOSITO DE FIBRA DE CARBONO
Vocabulário
[pt] CONCRETO
Vocabulário
[en] STRUCTURAL STRENGTHENING
Vocabulário
[en] BOND
Vocabulário
[en] CARBON FIBER COMPOSITE
Vocabulário
[en] CONCRETE
Resumo
[pt] É descrito neste trabalho um programa experimental sobre a
aderência entre os
compósitos com tecido de fibras de carbono e o concreto.
Este programa
experimental consistiu em ensaios de tração-compressão de
corpos-de-prova
compostos de dois blocos de concreto (móvel e fixo)
colados por tiras de tecido
de fibra de carbono coladas nos lados opostos desses
blocos. Foram ensaiados
nove corpos-de-prova, com três resistências à compressão
aos 28 dias de 20,5
MPa, 28,7 MPa e 38,1 MPa e duas larguras do tecido iguais
a 50 mm e 100 mm.
Todos os corpos-de-prova foram concretados, instrumentados
e ensaiados no
Laboratório de Estruturas e Materiais da PUC-Rio. O
objetivo deste trabalho foi
estudar a influência da resistência do concreto e da
largura do tecido de fibra de
carbono sobre a resistência de aderência do sistema. Os
resultados mostraram
que a resistência de aderência pode ser considerada
independente da resistência
do concreto e da largura do tecido. Foi obtido, neste
estudo, um valor
característico de 1,45 MPa para a resistência de aderência.
Resumo
[en] An experimental study on the bond between carbon fiber
fabric composites and
concrete is described in this work. This experimental
program consisted of
tension-compression tests of specimens with two concrete
blocks (movable and
fixed) jointed by carbon fiber fabric strips bonded on two
opposite sides of these
blocks. Nine specimens, with three concrete compressive
strength of 20,5MPa ,
28,7MPa and 38,1MPa at 28 days and two fabric width of 50
mm and 100
mm, were tested. All specimens had the same geometrical
characteristics. All the
specimens were cast, instrumented and tested in the
Structural and Materials
Laboratory at PUC-Rio. The objective of this work was to
study the influence of
concrete strength and the width of the fabric on the bond
strength of the system.
The results showed that the ultimate bond strength may be
considered
independent of concrete strength and of the width of the
fabric. A characteristic
value of 1.45 MPa was found for the bond strength.
Orientador(es)
GIUSEPPE BARBOSA GUIMARAES
Coorientador(es)
EMIL DE SOUZA SANCHEZ FILHO
Banca
GIUSEPPE BARBOSA GUIMARAES
Banca
MARTA DE SOUZA LIMA VELASCO
Banca
EMIL DE SOUZA SANCHEZ FILHO
Banca
ROBSON LUIZ GAIOFATTO
Banca
MARIA ELISABETH DA NOBREGA TAVARES
Catalogação
2006-01-02
Apresentação
2005-06-10
Tipo
[pt] TEXTO
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Idioma(s)
PORTUGUÊS
Referência [pt]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=7634@1
Referência [en]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=7634@2
Referência DOI
https://doi.org/10.17771/PUCRio.acad.7634
Arquivos do conteúdo
CAPA, AGRADECIMENTOS, RESUMO, ABSTRACT, SUMÁRIO E LISTAS PDF CAPÍTULO 1 PDF CAPÍTULO 2 PDF CAPÍTULO 3 PDF CAPÍTULO 4 PDF CAPÍTULO 5 PDF REFERÊNCIAS BIBLIOGRÁFICAS E ANEXOS PDF