Título
[pt] ANÁLISE POR XPS E AFM DA SUPERFÍCIE DE BLENDAS DE PVC/PHB
Título
[en] XPS AND AFM ANALYSIS OF PVC/PHB BLENDS SURFACES
Autor
[pt] CLARA MUNIZ DA SILVA DE ALMEIDA
Vocabulário
[pt] ESPECTROSCOPIA
Vocabulário
[pt] PHB
Vocabulário
[pt] FORCA ATOMICA
Vocabulário
[pt] MICROSCOPIA
Vocabulário
[pt] BLENDAS
Vocabulário
[pt] RAIOS-X
Vocabulário
[en] SPECTROSCOPY
Vocabulário
[en] PHB
Vocabulário
[en] ATOMIC FORCE
Vocabulário
[en] MICROSCOPY
Vocabulário
[en] BLENDS
Vocabulário
[en] X-RAY
Resumo
[pt] Neste trabalho, foram estudadas blendas formadas pelo
polímero
Policloreto de Vinila (PVC) e pelo polímero biodegradável
Poli Hidroxibutirato
(PHB), com diferentes concentrações relativas de cada
polímero. As blendas
foram preparadas em forma de membrana, com concentrações
de PHB variando
de 2 a 40%. A técnica utilizada para o preparo das
amostras foi a evaporação do
solvente, sendo dicloroetano o solvente utilizado. A
composição química das
superfícies das blendas foi caracterizada utilizando a
técnica de espectroscopia de
fotoelétrons induzida por raios-X (XPS). A morfologia e as
propriedades
mecânicas das amostras foram estudadas com o auxílio da
microscopia de força
atômica (AFM). Medidas de calorimetria diferencial
exploratória foram realizadas
a fim de conhecermos a miscibilidade das blendas formadas.
Nas blendas
formadas observou-se uma segregação de PHB para a
superfície, sendo o
percentual de PHB na superfície na faixa de 18±2%, mesmo
para blendas com
mais baixa concentração relativa de PHB. Entretanto o grau
de cristalização do
PHB em cada blenda aumenta com a incorporação do polímero
na blenda. Foi
observado um aumento na dureza conforme aumentamos a
concentração de PHB
na blenda. As blendas foram caracterizadas como
parcialmente miscíveis.
Resumo
[en] In this work, the study of polymer blends surfaces formed
by a
biodegradable polymer (poly3-hydroxybutyrate, PHB) and PVC
(polyvinyl
chloride) with different molar percentages of PHB is
presented. The blends
samples were prepared as membranes with PHB molar
concentrations from 2 to
40%. The technique used to prepare the membranes was the
solvent-casting
technique, using dichloroethene as solvent. The chemical
composition of the
blends samples surfaces were characterized by X-ray
photoelectron spectroscopy
(XPS). Their morphologies and mechanical properties were
studied by atomic
force microscopy (AFM). Differential scanning calorimeter
measures were
obtained in order to know the blends miscibility. A PHB
surface segregation of
18±2% was observed, even for the blends with lower PHB
concentrations.
However, the degree of the PHB crystallization in each
blend increases with the
increasing incorporation of PHB in the blend volume. An
increase in the blends
hardness was observed while the PHB blends concentration
increases. The blends
were founded to be partially miscible.
Orientador(es)
RODRIGO PRIOLI MENEZES
Coorientador(es)
RUBEN JESUS SANCHEZ RODRIGUEZ
Banca
GILSON BRAND BAPTISTA
Banca
RODRIGO PRIOLI MENEZES
Banca
RUBEN JESUS SANCHEZ RODRIGUEZ
Banca
SUZANA ISABEL ZANETTE DE CARIDE
Catalogação
2005-10-25
Apresentação
2005-03-29
Tipo
[pt] TEXTO
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Idioma(s)
PORTUGUÊS
Referência [pt]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=7338@1
Referência [en]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=7338@2
Referência DOI
https://doi.org/10.17771/PUCRio.acad.7338
Arquivos do conteúdo
CAPA, AGRADECIMENTOS, RESUMO, ABSTRACT, SUMÁRIO E LISTAS PDF CAPÍTULO 1 PDF CAPÍTULO 2 PDF CAPÍTULO 3 PDF CAPÍTULO 4 PDF REFERÊNCIAS BIBLIOGRÁFICAS PDF