[en] USE OF BIOSURFACTANTS MIXTURE EXTRACTED FROM RHODOCOCCUS OPACUS AND RHODOCOCCUS ERYTHROPOLIS IN DIRECT FLOTATION OF IRON ORE FINES

[pt] USO DE MISTURAS DE BIOSSURFACTANTES EXTRAÍDOS DAS BACTÉRIAS RHODOCOCCUS OPACUS E RHODOCOCCUS ERYTHROPOLIS NA FLOTAÇÃO DIRETA DE FINOS DE MINÉRIO DE FERRO

[pt] IAN MONTEIRO WERNER

[pt] BIOFLOTACAO

[pt] BIOSURFACTANTES

[pt] RHODOCOCCUS ERYTHROPOLIS

[pt] RHODOCOCCUS OPACUS

[pt] MINERIO DE FERRO

[en] BIOFLOTATION

[en] BIOSURFACTANTS

[en] RHODOCOCCUS ERYTHROPOLIS

[en] RHODOCOCCUS OPACUS

[en] IRON ORE

[pt] O aumento da demanda mundial por matérias primas minerais e a eventual redução do teor do mineral de interesse aliado à complexidade mineralógica tem levado as empresas vinculadas ao setor mineral a considerar o processamento de minérios com as características mencionadas anteriormente. Sob essa ótica, os biossurfactantes vêm ganhando destaque por possuirem atividade semelhantes aos surfactantes sintéticos com o benefício adicional de uma toxicidade menor. Além disso, a mistura de reagentes pode gerar maior seletividade quando comparado ao uso de um único coletor. Inclusive, pode haver a necessidade de empregar uma quantidade menor de surfactante para alcançar a mesma recuperação, dessa forma, reduzindo o custo de produção e a poluição ambiental. O uso de misturas de biossurfactantes ainda não foi considerado para tal propósito. O objetivo principal dessa pesquisa é avaliar a mistura dos biossurfactantes extraídos das bactérias Rhodococcus opacus e Rhodococcus erythropolis como coletores de hematita na flotação direta do rejeito de minério de ferro. Assim, espera-se que a mistura de biossurfactantes seja mais seletiva aos minerais de ferro e recupere mais ferro que em seu uso individual. Foram feitos estudos de caracterização do minério de ferro: análise elementar e avaliação da interação entre biossurfactante e mineral. Ensaios de flotação serão realizados variando a concentração (1000 - 3000 g/t) e proporções de biossurfactantes (100 - 0 por cento). Os resultados obtidos mostraram . Os espectros de FTIR evidenciaram a adsorção do biossurfactante na superfície mineral, sendo essa de natureza eletrostática. O biossurfactante adsorvido aumentou o ângulo de contato da hematita de 40 graus para entre 60 graus e 70 graus. Os ensaios de flotação alcançaram um teor de 48.8 por cento de ferro e uma recuperação de 70 por cento.

[en] As the demand for raw materials increases and the ore content decreases, it generates a need to process ores with a higher degree of complexity and lower content of the mineral of interest. From this perspective, biosurfactants have been gaining prominence because they have similar activity to synthetic surfactants with the added benefit of lower toxicity. In addition to that, mixing different reagents may generate greater selectivity when compared to using a single collector. Also a smaller amount of surfactant may be needed to achieve the same recovery, thus reducing production cost and environmental pollution. The use of biosurfactant mixtures has not yet been considered for this purpose. The main objective of this research is to evaluate the mixture of biosurfactants extracted from the bacteria Rhodococcus opacus and Rhodococcus erythropolis as collectors of hematite in the direct flotation of iron ore tailings. Thus, it is expected that the mixture of biosurfactants to be more selective and recover more iron than in their individual use. Characterization studies of iron ore were carried out: elemental analysis and evaluation of the interaction between biosurfactant and mineral. Flotation tests will be carried out varying the concentration (1000 - 3000 g/t) and proportions of biosurfactants (100 - 0 per cent). The isoelectric point of hematite was around pH 5.3, while the PIE of quartz is below pH 2.0. The hematite/biosurfactant interaction shifted the PIE to around pH 3.5. As for the quartz/biosurfactant interaction, it was not possible to observe a change in the PIE. The FTIR spectra demonstrate the adsorption of the biosurfactant on the mineral surface, which is of an electrostatic nature. The adsorbed biosurfactant increased the hematite contact angle from 40 degrees to between 60 degrees and 70 degrees. The flotation tests reached an iron content of 48.8 per cent and a recovery of 70 per cent.

MAURICIO LEONARDO TOREM

RONALD ROJAS HACHA

MAURICIO LEONARDO TOREM

ANA ROSA FONSECA DE AGUIAR MARTINS

ANTONIO GUTIERREZ MERMA

HUDSON JEAN BIANQUINI COUTO

RONALD ROJAS HACHA

2025-05-23

2022-09-30

[pt] TEXTO

application/pdf

PORTUGUÊS

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=70570@1

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=70570@2

https://doi.org/10.17771/PUCRio.acad.70570