[en] FRACTOGRAPHIC PRACTICES IN THE FORENSIC ANALYSIS OF REAL CASE OF MECHANICAL FAILURE DUE TO FATIGUE DAMAGE

[pt] PRÁTICAS FRATOGRÁFICAS NA ANÁLISE PERICIAL DE CASO REAL DE FALHA MECÂNICA POR FADIGA

[pt] PEDRO ANTUNES BUSTAMANTE

[pt] FADIGA

[pt] ANALISE DE FALHAS

[pt] FRATOGRAFIA

[pt] ENGENHARIA FORENSE

[pt] METALOGRAFIA

[en] FATIGUE

[en] FAILURE ANALYSIS

[en] FRACTOGRATHY

[en] FORENSIC ENGINEERING

[en] METALLOGRAPHY

[pt] Um acidente mecânico gera perdas humanas e/ou materiais, em geral. A causa dele pode culpabilizar ou não indivíduos envolvidos no funcionamento daquele sistema, seja no projeto, fabricação e montagem, seja na inspeção periódica, ou mesmo no seu manuseio. Judicializado o caso, se não há testemunhas, ou se as há, mas com conflitos de interesse, o Engenheiro Forense entra em cena e, tomando conhecimento do que se sabe a posteriori do fato, ligará a estas informações a história da vida que o resíduo material deixou registrada em si, e produzirá um laudo com parecer técnico do que parece ter ocorrido. Por isso, um bom Engenheiro Mecânico Forense deve ser também um bom estudioso de Fratografia, ou seja, da análise das características da fratura e o nexo causal provável entre o mecanismo causador da fratura do componente e a topografia da superfície fraturada. A Fratografia é um ramo vastíssimo de estudo, cujos registros iniciais remontam ao século XVI e que evoluiu para a atual Fratografia Eletrônica e Quantitativa, que permite relacionar, por exemplo, as marcas de estriamento com o provável ciclo de carregamento sofrido pelo componente. Neste trabalho, acidente real periciado, cuja falha mecânica deveu-se à fadiga, será revisitado e avaliado à luz de bibliografia específica: desde o entendimento do funcionamento original do sistema mecânico, passando por breve metalografia do material colapsado e depois por análise fratográfica e inferências físicas e matemáticas daí derivadas, até resultados e conclusões que - espera-se - acrescentem saber a profissionais que estejam aqui em busca de boas técnicas de análise para novos - e infelizes - acidentes.

[en] A mechanical accident generates human and/or material losses, in general. Its cause may or may not blame individuals involved in the operation of that system, whether in design, manufacture and assembly, or in periodic inspection, or even in its use. Once the case has been judicialized, if there are no witnesses, or if there are, but with conflicts of interest, the Forensic Engineer enters the scene and, taking knowledge of what is known a posteriori of the fact, will link to this information the history of the life that the residue material has registered itself, and will produce a report with a technical opinion of what seems to have occurred. Therefore, a good Forensic Mechanical Engineer must also be a good student of Fractography, that is, the analysis of fracture characteristics and the probable causal link between the mechanism causing the component fracture and the topography of the fractured surface. Fractography is a vast branch of study, whose initial records date back to the 16th century and which evolved into the current Electronic and Quantitative Fractography, which allows relating, for example, the groove marks with the probable loading cycle suffered by the component. In this work, real accident investigated, whose mechanical failure were due to fatigue, will be revisited and evaluated in the light of specific bibliography: from the understanding of the original functioning of the mechanical system, passing through a brief metallography of the collapsed material and then by fractographic analysis and inferences physics and mathematics derived therefrom, to results and conclusions that - it is hoped - add knowledge to professionals who are here in search of good analysis techniques for new - and unfortunate - accidents.

MARCO ANTONIO MEGGIOLARO

2024-12-19

[pt] TEXTO

application/pdf

PORTUGUÊS

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=68860@1

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=68860@2

https://doi.org/10.17771/PUCRio.acad.68860