[pt] COMPORTAMENTO MECÂNICO E ANÁLISE DA EVOLUÇÃO DO DANO EM CONCRETO REFORÇADO COM FIBRAS SOB FADIGA À FLEXÃO PARA APLICAÇÕES ESTRUTURAIS

[en] MECHANICAL BEHAVIOR AND DAMAGE EVOLUTION OF FIBER REINFORCED CONCRETE UNDER FLEXURAL FATIGUE LOADING FOR STRUCTURAL APPLICATIONS

[pt] VITOR MOREIRA DE ALENCAR MONTEIRO

[pt] CONCRETO ARMADO

[pt] DEGRADACAO MECANICA

[pt] MODELO ANALITICO

[pt] CONCRETO REFORCADO COM FIBRA

[pt] FADIGA

[en] REINFORCED CONCRETE

[en] MECHANICAL DEGRADATION

[en] ANALYTICAL MODEL

[en] FIBER REINFORCED CONCRETE

[en] FATIGUE

[pt] A presente tese de doutorado tem como origem o projeto de pesquisa Aneel PD-0394-1905/2019, realizado a partir de uma colaboração entre Furnas e PUC-Rio. A principal meta desse grande projeto de pesquisa está no desenvolvimento do concreto reforçado com fibras visando sua aplicação em elementos estruturais que estão submetidos à fadiga na flexão ao longo de toda sua vida útil, como torres eólicas, pavimentos e elementos de pontes. Dessa maneira, ao longo de todo essa tese doutorado, a degradação mecânica do concreto reforçado com fibras sob fadiga é analisada em detalhe desde a escala da fibra em ensaios de arrancamento até a escala estrutural através de testes mecânicos de fadiga em larga escala. A primeira etapa desse estudo traz uma análise do comportamento à fadiga do concreto reforçado com fibras. A vida à fadiga desse material é estudada através de diferentes modelos estatísticos, que garantem avaliar a falha do material baseada em uma probabilidade falha. Já os ensaios de fadiga no arrancamento ajudam a explicar na escala interface fibra-matriz como ocorre a ruptura dos prismas sob carregamentos cíclicos. Uma segunda fase desse trabalho mostra a degradação mecânica de vigas armadas sob fadiga e o impacto da adição de fibras nos principais parâmetros de interesse. A adição do reforço fibroso é responsável por causar uma redistribuição de tensões na zona tracionada do elemento estrutural, diminuindo as deformações da armadura longitudinal e amenizando a degradação mecânica do concreto armado em termos de curvatura, deslocamento e rigidez. Além disso, a adição de fibras também é responsável por incrementar significativamente a aderência da barra de aço ao redor da matriz de concreto. Fator chave para explicar a melhora da resposta mecânica da estrutura sob fadiga e estudada nessa tese de doutorado através dos ensaios de arrancamento da barra aço. Por fim, uma nova solução analítica foi desenvolvida para avaliar a degradação mecânica dos prismas de concreto reforçado com fibras sob fadiga. As curvas analíticas propostas se adequaram de forma bem sucedida os resultados experimentais analisados nesse trabalho. A adição de fibras apresentou grande potencial visando uma diminuição da degradação mecânica das estruturas de concreto armado submetidas a carregamentos cíclicos. A redistribuição de tensões na zona tracionada devido às fibras promove uma maior rigidez da estrutura sob fadiga, uma melhora da aderência da armadura e uma maior capacidade de resistir aos ciclos de fadiga ao longo do tempo. Esse ganho mecânico com o reforço fibroso, portanto, pode garantir maior vida útil das estruturas em concreto armado.

[en] This doctoral thesis originates from the research project Aneel PD-0394- 1905/2019, carried out through a collaboration between Furnas and PUC-Rio. The main objective of this extensive research project is the development of fiber reinforced concrete for distinct structural application which are subjected to continuous flexural fatigue loading along their useful life, such wind tower endeavors, concrete pavements and bridge elements. The addition of fibers in the concrete mix has the potential to mitigate the mechanical deterioration along the continuous load cycles, enhancing, as a consequence, the durability and the fatigue life of the cited concrete structural elements. Throughout this doctoral thesis, the mechanical degradation of fiber reinforced concrete under fatigue is carefully analyzed, starting from the fiber scale with pull-out tests and going up to the structural scale through large-scale fatigue mechanical tests. The first stage of this study involves an analysis of the mechanical behavior of fiber reinforced concrete under fatigue loading. The material fatigue life is examined using different statistical models, which allow evaluating material failure based on a failure probability. Fatigue pull-out tests help explain, at the fiber-matrix interface scale, how the prisms rupture under cyclic loading. A second phase of this work demonstrates the mechanical degradation of reinforced structural beams under fatigue and the impact of fiber addition on key concerned parameters. The addition of fiber reinforcement causes a redistribution of stresses in the tension zone of the structural element, reducing the deformations of the longitudinal rebar and mitigating the mechanical degradation of reinforced concrete in terms of curvature, displacement and stiffness. Furthermore, fiber addition significantly improves the bond between the steel bar and the surrounding concrete matrix, a key factor in explaining the enhanced mechanical response of the structure under fatigue, as studied in this doctoral thesis through rebar pull-out tests. Finally, a new analytical solution was developed to assess the mechanical degradation of fiber reinforced concrete prisms under fatigue loads. The proposed analytical curves successfully fit the experimental results analyzed in this work. The addition of fibers showed great potential in reducing the mechanical degradation of reinforced concrete structures subjected to cyclic loading. The stress redistribution in the tension zone, caused by the fibers, promotes greater stiffness of the structure under fatigue, improves the bond with the reinforcement and enhances the ability to withstand fatigue cycles over time. Therefore, the observed enhancement of mechanical properties through fiber reinforcement can ensure a longer service life for reinforced concrete structures.

FLAVIO DE ANDRADE SILVA

DANIEL CARLOS TAISSUM CARDOSO

FLAVIO DE ANDRADE SILVA

ELISA DOMINGUEZ SOTELINO

DANIEL CARLOS TAISSUM CARDOSO

PABLO AUGUSTO KRAHL

BARZIN MOBASHER

ALBERT DE LA FUENTE ANTEQUERA

2024-04-11

2023-12-04

[pt] TEXTO

application/pdf

INGLÊS

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=66414@1

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=66414@2

https://doi.org/10.17771/PUCRio.acad.66414