Título
[en] AGING ASSESSMENT OF STRUCTURAL GFRP PROFILES THROUGH NON-DESTRUCTIVE DYNAMIC TESTING
Título
[pt] AVALIAÇÃO DO ENVELHECIMENTO DE PERFIS ESTRUTURAIS DE PRFV UTILIZANDO ENSAIOS DINÂMICOS NÃO DESTRUTIVOS
Autor
[pt] JOAO PEDRO DE CASTRO TORRES
Vocabulário
[pt] ANALISE MODAL EXPERIMENTAL
Vocabulário
[pt] TECNICAS NAO DESTRUTIVAS
Vocabulário
[pt] PRFV
Vocabulário
[pt] DEGRADACAO
Vocabulário
[en] EXPERIMENTAL MODAL ANALYSIS
Vocabulário
[en] NON-DESTRUCTIVE TECHNIQUE
Vocabulário
[en] GFRP
Vocabulário
[en] DEGRADATION
Resumo
[pt] Nas últimas décadas, perfis pultrudados de polímeros reforçados com
fibra (PRF) vêm despertando grande interesse na indústria civil devido a
sua alta relação entre resistência e peso e sua aplicabilidade em
ambientes agressivos. Apesar de apresentar grande resistência às
intempéries, a degradação dos PRF foi notada após anos de exposição
em campo. A utilização de ensaios não destrutivos (END) se mostra
como uma boa alternativa para avaliar a integridade deste material,
havendo especial interesse para controle de qualidade de baixo custo
em campo. Dessa forma, este trabalho utilizou ensaios de vibração livre
com duas técnicas de excitação por impulso para detectar danos em
polímeros reforçados com fibra de vidro envelhecidos em câmaras com
elevada temperatura, umidade e salinidade. Através da avaliação das
frequências naturais e amortecimentos, foi observado o impacto das
condições ambientais na integridade do material, resultado corroborado
pela variação das propriedades elásticas obtidas através da resposta
dinâmica acústica.
Resumo
[en] In the last decades, pultruded profiles of fiber-reinforced polymers (FRP)
have been attracting great interest in the civil industry due to their high
strength-to-weight ratio and their applicability in aggressive environments.
Despite showing great resistance to weathering, the degradation of FRP
was noticed after years of exposure in the field. The use of non-destructive
techniques (NDT) has been shown to be a good alternative to evaluate the
integrity of this material, with special interest for low-cost quality control in
the field. Thus, this work used free vibration tests with two impulse excitation
techniques to detect damage in glass fiber reinforced polymers aged in
chambers with high temperature, humidity and salinity. Through the
evaluation of natural frequencies and damping, the impact of environmental
conditions on the integrity of the material was observed, a result
corroborated by the variation of elastic properties obtained through the
acoustic dynamic response.
Orientador(es)
DANIEL CARLOS TAISSUM CARDOSO
Coorientador(es)
CASSIO MARQUES RODRIGUES GASPAR
Banca
JANINE DOMINGOS VIEIRA
Banca
DANIEL CARLOS TAISSUM CARDOSO
Banca
CASSIO MARQUES RODRIGUES GASPAR
Banca
WENDELL DINIZ VARELA
Catalogação
2023-08-07
Apresentação
2022-04-28
Tipo
[pt] TEXTO
Formato
application/pdf
Idioma(s)
PORTUGUÊS
Referência [pt]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=63568@1
Referência [en]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=63568@2
Referência DOI
https://doi.org/10.17771/PUCRio.acad.63568
Arquivos do conteúdo
NA ÍNTEGRA PDF