Título
[en] PROPERTIES OF MO-SNO2 CATALYSTS AND THE EFECT OF SODIUM ADDITION
Título
[pt] PROPRIEDADES DE CATALISADORES DE MO-SNO2 E O EFEITO DA ADIÇÃO DE SÓDIO
Autor
[pt] ISAQUE CARDOSO DA SILVA
Vocabulário
[pt] CARACTERIZACAO
Vocabulário
[pt] SOLIDOS ACIDOS
Vocabulário
[pt] SODIO
Vocabulário
[pt] DIOXIDO DE ESTANHO
Vocabulário
[pt] ESPECIES DE MOLIBDENIO
Vocabulário
[en] CHARACTERIZATION
Vocabulário
[en] ACIDIC SOLIDS
Vocabulário
[en] SODIUM
Vocabulário
[en] TIN DIOXIDE
Vocabulário
[en] MOLYBDENUM SPECIES
Resumo
[pt] Catalisadores Mo-SnO2 foram obtidos a partir da
precipitação, em solução
aquosa, do SnO2.xH2O na presença de (NH4)2Mo7O24 em dois
teores de Mo:
5,5 e 14,5 por cento em massa, os quais foram, posteriormente,
impregnados com 1 por cento
em massa de cátion sódio. Os sólidos obtidos foram
caracterizados por
espectroscopia de reflectância difusa na região do UV-
visível, difração de
raios-X, adsorção de nitrogênio, redução à temperatura
programada, e
espectroscopia de absorção na região do infravermelho de
metanol e de
piridina adsorvidos. Verificou-se que a presença de sódio
resulta na diminuição
da área específica, na eliminação dos microporos e dos
poros de diâmetro
elevado, sendo os últimos referentes aos polimolibdatos.
Verificou-se, também,
que a presença de sódio propicia o consumo das espécies
dispersas de
molibdênio, resultando na sua aglomeração, com formação de
polimolibdatos.
Com relação à acidez dos sólidos, verificou-se que a ação
do Na é função da
concentração superficial de Mo. No caso de baixa
concentração de Mo,
observou-se que o sódio promove a eliminação dos sítios de
Brönsted e a
formação de sítios fracos de Lewis; já para a concentração
elevada, observouse,
além da formação de sítios fracos de Lewis, um aumento da
concentração
dos sítios de Brönsted. Assim, o Na altera de forma
significativa a textura, a
acidez e as espécies de Mo presentes nos catalisadores Mo-
SnO2.
Resumo
[en] Mo-SnO2 catalysts were prepared by SnO2.xH2O precipitation
with ammonium
heptamolybdate solution. Two Mo amounts were used: 5,5 and
14,5 percent (wt);
Afterwards, these samples were impregnated with 1 percent Na
(wt). These solids
were characterized by nitrogen adsorption, UV-visible
diffuse reflectance
spectroscopy, temperature programmed reduction, X-ray
diffraction, infrared
spectroscopy of adsorbed pyridine and methanol. It was
observed that the Na
addition decreases the surface area of the Mo-SnO2 solids,
caused by
elimination of the micropores and the large pores of
polymolybdates. It was
also verified that Na promotes the agglomeration of Mo
species, i.e. the amount
of Mo dispersed species decreases and the polymolybdate one
increases.
Sodium also changes the solid acid properties: for the low
Mo amount it was
observed that Na promoted the formation of weak Lewis acid
sites and the
elimination of Brönsted sites; on the other hand for the
high Mo amount, both
Brönsted and weak Lewis acid sites content increased when
Na was added.
These results showed that sodium changed the texture, the
Mo species and the
acid properties of Mo-SnO2 catalysts.
Orientador(es)
SILVANA BRAUN
Coorientador(es)
LUCIA GORENSTIN APPEL
Banca
SILVANA BRAUN
Banca
LUCIA GORENSTIN APPEL
Banca
ALEXANDRE CARLOS CAMACHO RODRIGUES
Banca
LUCIA REGINA RADDI DE ARAUJO
Banca
MARIA CONCEICAO GRECA
Catalogação
2005-03-10
Apresentação
2004-08-31
Tipo
[pt] TEXTO
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Formato
application/pdf
Idioma(s)
PORTUGUÊS
Referência [pt]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=6045@1
Referência [en]
https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=6045@2