[pt] DESENVOLVIMENTO E CARACTERIZAÇÃO DE COMPÓSITOS VERDES PARA HABITAÇÕES SOCIAIS

[en] DEVELOPMENT AND CHARACTERIZATION OF GREEN COMPOSITES FOR SOCIAL HOUSING

[pt] NATALIA VICTORIA DOS SANTOS

[pt] FIBRAS VEGETAIS

[pt] HABITACOES SOCIAIS

[pt] BIOCOMPOSITO

[pt] IMPRESSAO 3D

[pt] MATERIAL COMPOSITO

[en] VEGETABLE FIBRES

[en] SOCIAL HOUSING

[en] BIOCOMPOSITE

[en] 3D PRINTING

[en] COMPOSITE MATERIAL

[pt] Os profissionais da construção civil vêm se tornando mais conscientes sobre seu papel no agravamento dos problemas ambientais, levando estes à procura de métodos e materiais que apresentem menos impacto ambiental. O uso de fibras vegetais como reforço vem sendo feito ao longo dos anos de forma a melhorar as propriedades mecânicas de compósitos, sendo estas de caráter renovável e biodegradáveis. A presente pesquisa visa a caracterização de biocompósitos para fabricação de habitações sociais de baixo impacto ambiental através do processo de moldagem por compressão das placas de vedação de tecido de fibra de juta e matriz de poliuretano vegetal e de impressão 3D de perfis e ligações de PLA e fibra vegetal de juta, sisal e rami. Para as placas moldadas por compressão foi feito um estudo da influência da direção da fibra nas propriedades mecânicas, constatando, através de ensaio de flexão monotônica, que a direção principal da fibra (urdume do tecido) apresenta a melhor resistência e maior rigidez, alcançando 37,2 mais ou menos 0,9MPa e 10,4 mais ou menos 1,1GPa, respectivamente. Analisando os efeitos à longo prazo, foi estudado o efeito da radiação ultravioleta nas placas, onde foram feitos ensaios em corpos de prova nas direções 0 graus e 90 graus expostos a uma lâmpada ultravioleta de 365nm por 3 (três) meses. Além disso, com os resultados dos ensaios foi possível aplicar a regra das misturas de forma inversa na determinação das propriedades da fibra e da matriz. Para os compósitos impressos 3D foi analisada a influência do tipo de fibra na resistência à tração e rigidez do material. Pelo ensaio à tração foram constatados aumentos significativos na resistência com o uso de fibras de rami (61,8 por cento) e sisal (110,8 por cento), chegando à resistência de 45,5 mais ou menos 6,1MPa e 59,3 mais ou menos 4,1MPa, respectivamente.

[en] Civil construction professionals have become more aware of their role in aggravating environmental problems, leading them to search for methods and materials that have less environmental impact. Vegetable fibers have been used as reinforcement over the years to improve the mechanical properties of composites, which are renewable and biodegradable. This research aims at the characterization of biocomposites for social housing manufacture with low environmental impact through the sealing plates compression molded process of jute fiber fabric and vegetable polyurethane matrix and 3D printing of PLA profiles and connections of jute, sisal, and ramie vegetable fiber. For the compression molded plates, a study was made to determine the influence of fiber direction on mechanical properties, noting, through a monotonic bending test, that the main fiber direction (warp of the fabric) has the highest resistance and stiffness, with 37.2 plus or minus 0.9MPa and 10.4 plus or minus 1.1GPa, respectively. Analyzing long term effects, the plates were exposed to ultraviolet radiation. In these tests, the specimens were exposed to a 365nm ultraviolet lamp during three months before being submitted to directional resistance trials in 0 degrees and 90 degrees. Furthermore, with the test results, it was possible to apply the mixing rule inversely to determine the fiber and matrix properties. For 3D printed composites, the influence of fiber type on the material s tensile strength and stiffness was analyzed. The tensile test found significant increases in strength with the use of ramie (61.83 percent) and sisal (110.80 percent) fibers, reaching a strength of 45.5 plus or minus 6.1MPa and 59.3 plus or minus 4.1MPa, respectively.

DANIEL CARLOS TAISSUM CARDOSO

GLAUCO JOSE DE OLIVEIRA RODRIGUES

FLAVIO DE ANDRADE SILVA

JOSE ROBERTO MORAES D ALMEIDA

GLAUCO JOSE DE OLIVEIRA RODRIGUES

DANIEL CARLOS TAISSUM CARDOSO

2021-09-14

2021-07-30

[pt] TEXTO

application/pdf

PORTUGUÊS

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=54716@1

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=54716@2

https://doi.org/10.17771/PUCRio.acad.54716