[en] ANALYSIS STEEL PARTS OF COMPARATIVE OBTAINED BY FOUNDRY OR 3D PRINTING: DIMENSIONAL MICROCT FOR ANALYSIS AND CHARACTERISTICS OF MECHANICAL PROPERTIES

[pt] ANÁLISE COMPARATIVA DE PEÇAS DE AÇO OBTIDAS POR FUNDIÇÃO OU IMPRESSÃO 3D: ANÁLISE TRIDIMENSIONAL POR MICROCT E CARACTERIZAÇÃO DAS PROPRIEDADES MECÂNICAS

[pt] MAYARA GUILHERME MARZANO

[pt] MICROTOMOGRAFIA

[pt] IMPRESSAO 3D

[en] MICROTOMOGRAPHY

[en] 3D PRINTING

[pt] As novas técnicas de manufatura aditiva, tais como impressão 3D, permitem criar peças metálicas com formas variadas facilitando a prototipação de diferentes componentes. No entanto, pouco se sabe ainda sobre a microestrutura das peças impressas e sobre suas propriedades mecânicas. Neste trabalho, peças de aço obtidas pelo processo tradicional de fundição e usinagem foram comparadas com peças obtidas por impressão 3D, ambas de mesma composição química. Para isso, utilizou-se microtomografia de raios-x, tecnologia esta que permite fazer análises não destrutivas, e microscopia ótica para caracterização da microestrutura. Ensaios mecânicos como teste de tração e microdureza foram empregados para análise das propriedades mecânicas dos materiais devido ao distinto processo de fabricação. Através destas análises concluiu-se que a peça impressa apresenta maior resistência a tração quando comparada com a fundida, essa diferença é devido ao processo de fabricação diverso, explicado através da formação distinta de microestrutura das peças.

[en] The new additive manufacturing techniques, such as 3D printing, allow you to create metal parts with varied shapes facilitating the prototyping of different components. However, do not exists many knowledge about the microstructure of printed pieces and on its mechanical properties. In this paper, steel parts obtained by the traditional process of casting and machining were compared with obtained by 3D printing pieces, both of the same chemical composition. For this, we used x-ray microtomography, this technology that allows non-destructive analysis, and optical microscopy to characterize the microstructure. Mechanical tests such as tensile test and hardness were employed for the analysis of mechanical properties of materials due to different manufacturing process. Through these analyzes it was concluded that the printed part has a higher tensile strength compared with the melt, this difference is due to a manufacturing process explained by formation of different parts of the microstructure.

SIDNEI PACIORNIK

MARCOS HENRIQUE DE PINHO MAURICIO

ANA ROSA FONSECA DE AGUIAR MARTINS

2015-09-29

[pt] TEXTO

application/pdf

PORTUGUÊS

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=25264@1

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=25264@2

https://doi.org/10.17771/PUCRio.acad.25264