[pt] INCORPORAÇÃO DE FÓSFORO EM NANOTUBOS DE CARBONO DE PAREDE SIMPLES PRODUZIDOS POR CVD EM ALTO VÁCUO

[en] PHOSPHORUS INCORPORATION IN SINGLE WALL CARBON NANOTUBES PRODUCED BY HIGH VACUUM CVD

[pt] CESAR AUGUSTO DIAZ MENDONZA

[pt] XPS

[pt] FOSFORO

[pt] NANOTUBOS DE CARBONO

[pt] ESPECTROSCOPIA RAMAN

[en] XPS

[en] PHOSPHORUS

[en] CARBON NANOTUBES

[en] RAMAN SPECTROSCOPY

[pt] Neste trabalho estudamos a síntese e caracterização de nanotubos de carbono de paredes simples com incorporação de fósforo. Os nanotubos foram produzidos em duas diferentes temperaturas (800 e 850 Graus Celsius), usando um precursor em pó (fase sólida) sem diluição em nenhum liquido. O sistema utilizado na síntese foi o CVD em alto vácuo. Para a caracterização comparamos as amostras incorporadas com SWNTs crescidos com etanol. Usamos a espectroscopia Raman, espectroscopia de fotoelétrons induzida por raios x (XPS) e microscopia eletrônica de transmissão (TEM) para caracterizar as amostras. A espectroscopia Raman e a microscopia eletrônica de transmissão foram usadas para confirmar a presença de SWNTs na amostra. Encontramos evidencia de que o fósforo foi incorporado nas amostras ao compararmos os espectros Raman dos SWNTs com amostra de referência. A partir dos resultados de XPS, observamos a presença de fósforo ligado a átomos de carbono que nós faz concluir que houve incorporação de fósforo nos nanotubos.

[en] In this work was studied the synthesis and characterization of single wall carbon nanotubes (SWCN) with phosphorus incorporation. The nanotubes were produced in two different temperatures (800 and 850 Degrees Celsius), using a powder precursor (solid phase) without liquid dilution. The system used for the synthesis was High Vacuum Chemical Vapor Deposition (HVCVD). The samples were characterized comparing the samples with phosphorus with SWNT synthetized with ethanol. Raman spectroscopy, x-ray photoelectron spectroscopy (XPS) on transmission electron microscopy (TEM) were employed to characterize the samples. The Raman spectroscopy and TEM were employed to confirm the presence of SWNT in the samples. We found evidences that phosphorus were incorporated comparing the Raman spectra with the reference sample. The XPS results showed the presence of phosphorus atoms bonded to carbon atoms which make us conclude that the phosphorus were incorporated to the nanotubes.

MARCELO EDUARDO HUGUENIN MAIA DA COSTA

FERNANDO LAZARO FREIRE JUNIOR

MARCELO EDUARDO HUGUENIN MAIA DA COSTA

FERNANDO LOUREIRO STAVALE JUNIOR

2015-03-10

2014-06-05

[pt] TEXTO

application/pdf

PORTUGUÊS

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=24237@1

https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=24237@2

https://doi.org/10.17771/PUCRio.acad.24237