This work aims to evaluate the shear strength of reinforced concrete beams with glass fiber reinforced polymer bars and to investigate qualitatively the contribution of the different shear transfer mechanisms to the final strength of the beam. An experimental program was conducted, including material characterization, dowel action tests, push-off tests, and finally, four-point bending tests on beams. Different parameters were investigated, such as the number of longitudinal bars for dowel action effect, maximum size of the coarse aggregate for aggregate interlock and the presence of stirrups for the beam tests. The monitoring of the development of the critical crack was performed with the aid of digital image correlation (DIC). The results showed that there was no difference in the behavior of the dowel action effect and the aggregate interlock through the tests performed. For beam tests, it was observed that all the specimens exhibited a concrete diagonal tension failure and for beams without stirrups, dowel action seemed to provide significant contribution to the shear strength after the crack, when the load reduces and the deflections increases, resulting from the loss of aggregate interlock as the crack opens. It was also observed that the presence of stirrups increased up to three times the shear strength of the beams tested and that there was rupture of the stirrup at the bent region.