The present study had as objectives to evaluate the influence of metallurgical heterogeneities on the fatigue cracking propagation threshold and to present alternative materials for the manufacture of crankshafts of diesel / natural gas engines of thermoelectric plants generating units, since such components mechanics manufactured with DIN 34CrNiMo6 steel has been presenting faults due to fatigue with a low number of loading cycles. Test specimens were machined from SAE 4140, SAE 4340 and DIN 42CrMo4 steels. Initially, tensile tests were conducted to determine the mechanical properties of the materials. Fatigue crack propagation tests were performed on C(T) specimens subjected to cyclic loading. Fatigue pre-cracks, with lengths ranging from 1.3 mm to 1.6 mm, were induced in the test specimens according to ASTM E647. In sequence, da/dN versus delta K curves of the materials were raised, with emphasis on the determination of the tensile strength factor of the propagation threshold (delta Kth) of each steel. In this context, the steel SAE 4140 presented a value of (delta Kth) superior to the others, which means to support larger crack sizes before the beginning of the propagation. Analysis by microscopy techniques evidenced the presence of inclusions in the region of crack propagation, giving rise to a preferential path for their growth. The results of these analyzes indicated the presence of a smaller number of inclusions in the steel SAE 4140, allowing an association of this microstructural characteristic with the value of the delta Kth of the material. In this way, with regard to the initiation of fatigue cracks, the SAE 4140 steel is presented as a viable alternative for the replacement of 34CrNiMo6 steel in the manufacture of crankshafts for motors of thermoelectric power plants.